| Magnus Table Tennis Table Plywood is a highly dense, compressed and thermoset plastic resin treated panel. The veneers are rotary cut then processed with high degree polymerized resin under heavy tonnage compression in a molding hot press. Cooling under compression pressure results in a hard, plain surface with excellent bouncing strength. Suitable for: Sports equipment like table tennis and billiard tables, chairs and seating, paneling and more. Product formats Thickness: 8, 12, 15, 18, 25, 30, 35, 40, 50, 62.5, 75, 80 mm Size[in feet]: 5×5, 6×5, 7×5, 8×5, 9×5, 10×5, 10.5×5.5 Density: 0.95 to 1.25 gm/cm3 Adhesive: BWP grade, IS 848 : 2006 Wood species: High density hardwood |
  |
| TECHNICAL SPECIFICATIONS | |||
| Properties | BIS Requirement IS 3513:1989 | Observation Values | |
| 1. | Length | 2440mm | 2442mm |
| 2. | Width | 1220mm | 1222mm |
| 3. | Thickness | 12mm | 12.10mm |
| 4. | Squareness | 2 % | 1mm |
| 5. | Edge straightness | 2 % | 0.95mm |
| 6. |
Density |
0.95 to 1.25 gm/cm2 | 1.00 gm/cm2 |
| 7. | Moisture content | 6 to 12 % | 7.50 % |
| Physical properties | |||
| 8 | Tensile strength | 59 Mpa | 142 Mpa |
| 9. | Static bending MOR | 59 Mpa | 180 Mpa |
| 10. | Compressive strength parallel to laminate | 75 Mpa | 125 Mpa |
| 11. | Perpendicular to laminate | 130 Mpa | 175 Mpa |
| 12. | Hardness test hardness on rockwell H scale | 60 | 65 |
| 13. | Impact strength parallel to laminate | 0.5 kg-M/cm2 | 0.57 kg-M/cm2 |
| 14. | Perpendicular to laminate | 0.2 kg-M/cm2 | 0.27 kg-M/cm2 |